PA610
Polyamide 610 (PA610) is created through poly-condensation of hexamethylene diamine and sebacic acid.
Hexamethylene diamine is obtained from crude oil, while sebacic acid is obtained following a multiple-step chemical process from the renewable bio-raw material castor oil. This means the polyamide 610 polymer is made to 62 per cent of renewable raw materials.
Special features of PA610 are:
use of 62% renewable basic raw materials (in relation to the polymer)
low water absorption and good dimensional stability compared to PA6 or PA66
good resistance to chemicals and weathering
high melting point of 215°C
problem-free processing
Due to its high melting point, PA610 is especially well suited for pipes, connectors and other under-the-hood automotive applications which are exposed to high temperatures. Further preferred applications are industrial pipes for pneumatic and hydraulic systems as well as sports and leisure.